Introduction:
Square Woven Fabric,also called Dipped T/C Narrow Fabric, woven by T/C yarns in both Warp and Weft direction. it’s a kind of reinforcement materials in rubber industries. Square woven fabric is SUPPLYRAM Star and Innovative products.
It has the characteristics of high strength, low elongation, dimensional stability, light weight, impact resistance, high temperature resistance, corrosion resistance, and good adhesion to rubber.
Technical Parameters:
NE16/1 * NE10/1 polyester /cotton yarn 65/35
| SIZE | ROLL LENGTH 300M +/-10 | ||||
|---|---|---|---|---|---|
| RAW MATERIAL | WARP :NE16/1 COTTON /POLYESTER 35/65 WEFT: NE10/1 COTTON/POLYESTER 35/65 | ||||
| TREATMENT | RFL | VALUES FOR ACCEPTANCE | |||
| CHARACTERISTIC | UNIT | NORMAL | MIN | MAX | |
| CONSTRUCTION-ENDS NUMBER | WARP | 190 | 185 | 195 | |
| WEFT | Yarns/dm | 95 | 90 | 100 | |
| Breaking loaD | Warp | 600 | 540 | ||
| Weft | N/5CM | 370 | 340 | ||
| Elongation at break | Warp | 15 | 10 | 20 | |
| Weft | % | 17 | 12 | 22 | |
| Weight | g/m2 | 180 | 170 | 190 | |
| Width | Mm | (*)TOLL+/-1 | |||
| Thickness | Mm | 0.48+/-0.05 | |||
| Wave | Tipo | TELA 1/1 | |||
| Shelf life | month | 12 | |||
Note: Special spec. can be customized by the requirement/sample from customers.
| SIZE | ROLL LENGTH 150M +/-10 | ||||
|---|---|---|---|---|---|
| RAW MATERIAL | WARP :NE30/1 COTTON /POLYESTER 35/65 WEFT: NE30/1 COTTON/POLYESTER 35/65 | ||||
| TREATMENT | RFL | VALUES FOR ACCEPTANCE | |||
| CHARACTERISTIC | UNIT | NORMAL | MIN | MAX | |
| CONSTRUCTION-ENDS NUMBER | WARP | Yarns/dm | 185 | 175 | 195 |
| WEFT | 80 | 75 | 85 | ||
| Breaking loaD | Warp | N/5CM | 270 | 240 | |
| weft | 110 | 90 | |||
| Elongation at break | Warp | % | 10 | 5 | 15 |
| weft | 17 | 12 | 22 | ||
| Weight | g/m2 | 80 | 75 | 85 | |
| Width | mm | (*)TOLL+/-1 | |||
| Thickness | Mm | 0.34+/-0.05 | |||
| Wave | Tipo | TELA 1/1 | |||
| Shelf life | mesi | 6 | |||
Note: Special spec. can be customized by the requirement/sample from customers.
Applications:
Square woven fabrics acting as a reinforcement materials are widely used in Hydraulic Rubber Hose production.